Ethylene-vinyl acetate copolymer
| Index Name | Specification |
|
| Appearance | White powder |
|
| Fluidity mm | 173 |
|
| Tensile propcrties(with cement mortar)original MPa | 0.84 |
|
| Tensile propcrties(with cement mortar)water resistence MPa | 0.96 |
|
| Tensile propcrties(with cement mortar)cold resistance MPa | 0.79 |
|
| Bending strength ratio % | 130 |
|
| Compression strength % | 103 |
|
| Time of coagulation h | Beginning | 7 |
| Final | 7.5 | |
| Percentage of contraction % | 0.035 |
|
| Index Name | Specification |
|
| Appearance | White powder |
|
| Fluidity mm | 173 |
|
| Tensile propcrties(with cement mortar)original MPa | 0.84 |
|
| Tensile propcrties(with cement mortar)water resistence MPa | 0.96 |
|
| Tensile propcrties(with cement mortar)cold resistance MPa | 0.79 |
|
| Bending strength ratio % | 130 |
|
| Compression strength % | 103 |
|
| Time of coagulation h | Beginning | 7 |
| Final | 7.5 | |
| Percentage of contraction % | 0.035 |
|